321 ומבאַפלעקט שטאָל סטריפּ
ומבאַפלעקט שטאָל בויגן פּלאַטע גראַדע באַאָגו צושטעלן
| טיפּ | גראַדע | גראַדע | כעמישער קאָמפּאָנענט % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | אנדערע | |||
| אַוסטעניטיק | 201 | SUS201 | ≤0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ≤0.060 | ≤0.030 | - | ≤1.00 | - | ≤0.25 | - |
| 202 | SUS202 | ≤0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0.060 | ≤0.030 | ≤1.00 | - | ≤0.25 | - | ||
| 301 | 1.431 | ≤0.15 | 16.00-18.00 | 6.00-8.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | ≤0.10 | - | |
| 304 | 1.4301 | ≤0.07 | 17.00-19.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304 ל | 1.4307 | ≤0.030 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304H | 1.4948 | 0.04-0.10 | 18.00-20.00 | 8.00-10.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309 | 1.4828 | ≤0.20 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309S | * | ≤0.08 | 22.00-24.00 | 12.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 310 | 1.4842 | ≤0.25 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| 310S | * | ≤0.08 | 24.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| 314 | 1.4841 | ≤0.25 | 23.00-26.00 | 19.00-22.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | 1.50-3.00 | - | - | - | |
| 316 | 1.4401 | ≤0.08 | 16.00-18.50 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316 ל | 1.4404 | ≤0.030 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316טי | 1.4571 | ≤0.08 | 16.00-18.00 | 10.00-14.00 | ≤2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | 0.1 | טי5(C+N)~0.70 | |
| 317 | * | ≤0.08 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 317 ל | 1.4438 | ≤0.03 | 18.00-20.00 | 11.00-15.00 | ≤2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 321 | 1.4541 | ≤0.08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | טי5(C+N)~0.70 | |
| 321H | * | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | טי5(C+N)~0.70 | |
| 347 | 1.455 | ≤0.08 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | נב≥10*C%-1.10 | |
| 347H | 1.494 | 0.04-0.10 | 17.00-19.00 | 9.00-12.00 | ≤2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | נב≥10*C%-1.10 | |
| xm-19 | ניטראָניק50 | ≤0.06 | 20.50-23.50 | 11.50-13.50 | 4.0-6.0 | ≤0.045 | ≤0.030 | 1.50-3.00 | ≤1.00 | - | 0.2-0.4 | נב: 0.10-0.30 וו: 0.10-0.30 | |
| 904 ל | N08904 | ≤0.02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | ≤0.045 | ≤0.035 | ≤1.00 | 0.1 | קו:1.0-2.0 | |||
| דופּלעקס | 2205 | S32205 | ≤0.03 | 22.0-23.0 | 4.5-6.5 | ≤2.00 | ≤0.030 | ≤0.020 | 3.0-3.5 | ≤1.00 | - | 0.14-0.20 | |
| 2507 | S32750 | ≤0.03 | 24.0-26.0 | 6.0-8.0 | ≤1.20 | ≤0.035 | ≤0.020 | 3.0-5.0 | ≤0.80 | 0.5 | 0.24-0.32 | ||
| * | S32760 | ≤0.03 | 24.0-26.0 | 6.0-8.0 | ≤1.00 | ≤0.030 | ≤0.010 | 3.0-4.0 | ≤1.00 | 0.5-1.00 | 0.2-0.3 | ||
| 2304 | S32304 | ≤0.03 | 21.5-24.5 | 3.0-5.5 | ≤2.50 | ≤0.040 | ≤0.030 | 0.05-0.6 | ≤1.00 | 0.05-0.6 | 0.05-0.2 | ||
| 329 | 1.446 | ≤0.08 | 23.00-28.00 | 2.00-5.00 | ≤1.00 | ≤0.040 | ≤0.030 | 1.00-2.00 | ≤0.75 | - | - | ||
| פערריטע | 409 | S40900 | ≤0.03 | 10.50-11.70 | 0.5 | ≤1.00 | ≤0.040 | ≤0.020 | - | ≤1.00 | - | ≤0.030 | Ti6(C+N)~0.50 נב:0.17 |
| 430 | 1קר17 | ≤0.12 | 16.00-18.00 | - | ≤1.0 | ≤0.040 | ≤0.030 | - | ≤1.0 | - | - | - | |
| 444 | S44400 | ≤0.025 | 17.50-19.50 | 1 | ≤1.00 | ≤0.040 | ≤0.030 | 1.75-2.5 | ≤1.00 | - | 0.035 | Ti+Nb:0.2+4(C+N)~0.80 | |
| 446 | S44600 | ≤0.20 | 23.00-27.00 | 0.75 | ≤1.5 | ≤0.040 | ≤0.030 | 1.50-2.50 | ≤1.00 | - | ≤0.25 | - | |
| מאַרטענסיטע | 410 | 1קר13 | 0.08-0.15 | 11.50-13.50 | 0.75 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0.080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 416 | Y1Cr13 | ≤0.15 | 12.00-14.00 | 3) | ≤1.25 | ≤0.060 | ≥0.15 | - | ≤1.00 | - | - | - | |
| 420 | 2Cr13 | ≥0.15 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0.26-0.35 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0.20 | 15.00-17.00 | 1.50-2.50 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤0.80 | - | - | - | |
| 440C | 11קר17 | 0.95-1.20 | 16.00-18.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | 0.75 | ≤1.00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0.07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | 3.00-5.00 | - | נב 0.15-0.45 |
| 631 | 17-7PH | ≤0.09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | ≤0.50 | - | על 0.75-1.50 | |
| 632 | 15-5PH | ≤0.09 | 14.00-16.00 | 3.50-5.50 | ≤1.00 | ≤0.040 | ≤0.030 | 2.00-3.00 | ≤1.00 | 2.5-4.5 | - | על 0.75-1.50 | |
באַשרייַבונג
321 ומבאַפלעקט שטאָל פּאַס איז אַ טיפּ פון אַוסטעניטיק ומבאַפלעקט שטאָל מיט נידעריק טשאַד אינהאַלט און גוט קעראָוזשאַן קעגנשטעל צו פילע קעראָוסיוו ינווייראַנמאַנץ.321 אָפפערס ויסגעצייכנט וועלדאַביליטי, גוט מאַשינאַביליטי און בוילעט פאַבריקיישאַן פּראָפּערטיעס.
321 ומבאַפלעקט שטאָל פּאַס איז קאַמאַנלי געניצט אין די כעמישער אינדוסטריע, פּאַפּ און פּאַפּיר אינדוסטריע, מאַרינע און אָפשאָר ינזשעניעריע ינדאַסטריז און אין די עסנוואַרג און בעוועראַגע ינדאַסטריז.
321 ומבאַפלעקט שטאָל פּאַס אויך האט אַ הויך קעגנשטעל צו קלאָרייד דרוק קעראָוזשאַן און פּיטינג.עס איז אויך קעגנשטעליק צו הידראָטשלאָריק זויער ביי עלעוואַטעד טעמפּעראַטורעס אַרויף צו 250 ° C (480 ° F).
איינריכטונגען
גוט קעראָוזשאַן קעגנשטעל: 321 ומבאַפלעקט שטאָל פּאַס האט בעסער קעראָוזשאַן קעגנשטעל ווי 304 און 316 טייפּס פון ומבאַפלעקט שטאָל, וואָס מאכט עס ידעאַל פֿאַר נוצן אין קעראָוסיוו ינווייראַנמאַנץ.
ויסגעצייכנט וועלדאַביליטי: 321 ומבאַפלעקט שטאָל פּאַס קענען זיין וועלדעד דורך אַלע מעטהאָדס אַרייַנגערעכנט קרייַזבויגן וועלדינג (TIG / GTAW), עלעקטראָן שטראַל וועלדינג (EBW / EFW), סאַבמערדזשד קרייַזבויגן וועלדינג (SAW) און לאַזער שטראַל וועלדינג (LBIW).
הויך סטרענגטה: די שטאַרקייַט לעוועלס פון 321 ומבאַפלעקט שטאָל פּאַס זענען אַרויף צו 50% העכער ווי די פון 304 טייפּס פון ומבאַפלעקט שטאָל און אַרויף צו 80% העכער ווי די פון 316 טייפּס פון ומבאַפלעקט שטאָל רעכט צו זייער געוואקסן טשאַד אינהאַלט און אַוסטעניטע קערל גרייס.